HIGH ELEVATION MATERIAL Cone Penetration 77°F (25°C) (ASTM D5329) 50-70 Resilience (ASTM D5329) 40% min. Softening Point (ASTM D36) 190°F (88°C) min. Ductility 77°F (25°C) (ASTM D113) 30 cm min. Flexibility (ASTM D3111 Modified) Pass at 0°F (-18°C) Flow 140°F (60°C) (ASTM D5329) 3 mm max. Brookfield Viscosity 400°F (204°C) (ASTM D2669) 100 Poise max. Asphalt Compatability (ASTM D5329) Pass Bitumen Content (ASTM D4) 60% min. Tensile Adhesion, 1” (ASTM D5329) 500% min. Recommended Application Temperature 380°F (193°C) Maximum Heating Temperature 400°F (204°C) 6 MODERATE ELEVATION MATERIAL Cone Penetration 77°F (25°C) (ASTM D5329) 35-55 Resilience (ASTM D5329) 40% min. Softening Point (ASTM D36) 200°F (93°C) min. Ductility 77°F (25°C) (ASTM D113) 30 cm min. Flexibility (ASTM D3111 Modified) Pass at 20°F (-7°C) Flow 140°F (60°C) (ASTM D5329) 3 mm max. Brookfield Viscosity 400°F (204°C) (ASTM D2669) 100 Poise max. Asphalt Compatability (ASTM D5329) Pass Bitumen Content (ASTM D4) 60% min. Tensile Adhesion, (ASTM D5329) 500% min. Minimum Application Temperature 380°F (193°C) Maximum Heating Temperature 400°F (204°C) LOW ELEVATION MATERIAL Cone Penetration (ASTM D5329) 20-40 Resilience (ASTM D5329) 30% min. Softening Point (ASTM D36) 210°F (99°C) min. Ductility 77°F (25°C) (ASTM D113) 30 cm min. Flexibility (ASTM D3111 Modified) Pass at 30°F (-1°C) Flow 140°F (60°C) (ASTM D5329) 3 mm max. Brookfield Viscosity 400°F (204°C) (ASTM D2669) 100 Poise max. Asphalt Compatability (ASTM D5329) Pass Bitumen Content (ASTM D4) 60% min. Tensile Adhesion, 1” (ASTM D5329) 400% min. Minimum Application Temperature 380°F (193°C) Maximum Heating Temperature 400°F (204°C) MEDIUM VISCOSITY MATERIAL Thermosel Viscosity at 400°F (204°C) (ASTM D4402) 4000 cp max Penetration 125°F (52°C), 50g, 5 sec. (ASTM D5) 50 max. Penetration 77°F (25°C), 100g. 5 sec. (ASTM D5) 10-25 Softening Point (ASTM D36) 210°F (99°C) min. Ductility 77°F (25°C) (ASTM D113) 15 cm min. Flexibility, 0°F (-18°C) Pass Minimum Application Temperature 380°F (193°C) Maximum Heating Temperature 420°F (216°C) . 7 LOW VISCOSITY MATERIAL Cone Penetration 77° F (25° C) (ASTM D5329) 35 max. Resilience 77° F (25° C) (ASTM D5329) 30% min. Softening Point (ASTM D36) 180°F (82°C) min. Ductility 77°F (25°C) (ASTM D113) 30 cm min. Flexibility 0° F (-18° C) 5 sec, 180° bend, ½” mandrel Pass Flow 140°F (60°C) 5h (ASTM D5329) 5 mm max. Brookfield Viscosity @ 375°F (191°C) (ASTM D4402) 2500-3500 cp Flash Point, COC 550°F (288°C) min. Minimum Application Temperature 380°F (193°C) Maximum Heating Temperature 400°F (204°C)