Specifications include, but are not limited to: WAX-TAPE PRIMER. PRIMER SHALL HAVE A PASTE-LIKE CONSISTENCY AND BE COMPOSED OF A BLEND OF PETROLEUM WAX, PLASTICIZER, AND CORROSION INHIBITORS. PRIMER SHALL BE BROWN IN COLOR, WITH A POUR POINT TEMPERATURE OF 100-110-DEGREES F, AND A FLASH POINT OF 350-DEGREES F MINIMUM. THE PRODUCT SHALL BE EASILY APPLIED BY HAND, WITH A COVERAGE RATE OF 100SF/GALLON, AND SHALL BE NON-TOXIC, NON-HAZARDOUS, AND NON-CARCINOGENIC, WITH NO VOCS. PRIMER SHALL BE COMPATIBLE WITH AND ENSURE ADHESION OF #1 TRENTON WAX-TAPE. "TRENTON" WAX-TAPE PRIMER, BROWN. EPOXY, "CANUSA HBE-95", BRUSH-GRADE, HIGH-BUILD EPOXY, PROTECTIVE COATING 1-L KIT SIZE SPECIFICATION: EPOXY, 100 % SOLIDS, TWO-COMPONENT SYSTEM, FOR USE AS A CORRSION PROTECTION COATING ON STEEL PIPELINE JOINTS AND FITTINGS. SHORE D HARDNESS = 85 MIN, ADHESION TO STEEL = 2000 PSI. MIN. CATHODIC DISBONDMENT RATING = 3 MM, RADIUS, MAX. AT 23C, 28-DAY, 8 MM, RADIUS, MAX. AT 95C, 28-DAY IMPACT = 26.5 IN-LB, MIN, AT 25C. HOT WATER IMMERSION = 1, EXCELLENT ( 1-5 RATING ), AT 75C, 28-DAY. WATER ABSORPTION = 0.1% MAX, DIELECTRIC STRENGTH = 400 VOLTS/MIL, MIN, CHEMICAL RESISTANCE = EXCELLENT, VARIOUS SOLUTIONS. FLASH POINT = 200F, MIN. POT LIFE = 15 MINUTES, 68F. CURE TIME = 4 HOURS, PRIOR TO HANDLING, AT 68F. CAN BE APPLIED BY BRUSH, ROLLER. OR GLOVE-APPLIED TO A MINIMUM THICKNESS OF 20 MILS. "CANUSA HBE-95"